Home  >  Properties & Comparison
 Comparison  
  MATERIAL COMPOSITION: (APPROXIMATE% OF MATERIALS)Reclaimed post production untrested hardwood (powder/granules)-60%
Reclaimed post consumer thermoplastics-P.P/HDPE/P.E(recyclable)-25%
New thermoplastics- P.P/HDPE/P.E(recyclable)-10%
Bonding agents/Resins-As per ASTM/BS Standards for WPC-5%

  DIFFERENCE BETWEEN COMPOSITE WOODIT, OTHER COMPOSITES & WOOD
Features WOODPRO Other composites wood
1. recyciable yes no no
Water absorption nill 0.8% and above 10% and above

PROPERTIES CONFIRMING STANDARDS STANDARDS UNITS
Tensile Strength ASTM D 638 15.9 Mpa
Flexural Modulus ASTM D 790 1582 Mpa
Failure Load ASTM D 1761 1.5 KN-20.8 KN
Heat Reversion BS EN 743: 1995 0.45%
Modulus of Elasticity ASTM D 6019 698.00psi
Modulus of Rupture ASTM D 6019 4.01psi
Flexural Strength ASTM D 6019 4017ps
Density ASTM D 6111 1.37g/cc
Coefficient of Friction(dry) ASTM D 2394 0.670
Coefficient of Friction(wet) ASTM D 2394 0.740
Coefficient of linear Thermal Expansion ASTM D 228 000015in/℉
Heat Deflection ASTM D 228 209℉
Water Absorption ASTM D 648 0.510
Screw Withdrawal ASTM D 1037 1.453ib
Termite Resistance AWPAFI-72 95
Fungal Resistance ASTM D 1413 No decay
Impact Strength ASTM D 1413 .957ftlbs/in
Compressive Strength-parallel ASTM D 198 5015psi
Shear Strength ASTM D 43 1482psi

  COMPARISON BETWEEN WOODPRO AND OTHER MATERIALS
Characteristics Wood Other Material KOMPOSITE WOODIT
Load Capacity ** * ***
Worked with Carpentry Tools *** * ****
Durability * ** ***
Water Absorption ** *** *
Weather Resistance * * ***
Chemical Resistance * **** ****
Low Maintenance ** * ***
Design Flexibility **** * ****